Virgin or Recycled PP Polypropylene Granules/PP Resin/PP Film/PP Injection Pellets/PP Random Copolymer

Model NO.: Polypropylene PP granules Color: Trasparent, White, Black CAS No.: 9003-07-0 Model: All Kinds of Medel Type: Virgin or Recycled Delviery: Within 15days After Confirming Trademark: FAN Origin: China Material: PP Item: Virgin or Recycled PP Polypropylene Granules/PP Re Place of Origin: China(Mainland) Shape: Granules Packaing: 25kg Woven Bag Sample: Free Sample Can Be Supplied Specification: SGS, ISO, CIQ HS Code: 3902100090 Virgin or Recycled PP Polypropylene Granules/PP Resin/PP Film/PP Injection Pellets/PP Random Copolymer
Specifications
pp granule 
1)virgin and recycled PP/Polypropylene granule 
2)fast delivery 
3) good impact resistance
(1)Injection or extrcsion grade , 
(2)Used for bags,plastic toy,container and bottles caps. 
(3)Good quality

Properties	Unit	Test method	Value
Melt Flow Rate
Melt flow rate(230°C/2.16KG)	g/10min	ISO 1133	12
Mechnical Properties
Tensile modulus of elasticity(v=1mm/min)	Mpa	ISO 527-2	1550
Tensile yield at stress(v=50mm/min)	Mpa	ISO 527-2	35
Tensile yield at strain (v=50mm/min)	%	ISO 527-2	8
Tensile strain at break (v=50mm/min)	%	ISO 527-2	>50
Charpy impact strength unnotched(+23°C)	kJ/m2	ISO 179/1eU	110
Charpy impact strength notched(+23°C)	kJ/m2	ISO 179/1eA	3.0
Izod Impact strength notenched(+23°C)	kJ/m2	ISO 180/1A	3
Ball indentation hardness(H 358/30)	Mpa	ISO 2039-1	78
Thermal Properties
Melting point,DSC	°C	ISO 3146	163
Heat deflection temperature (0.45Mpa)	°C	ISO 75-2	85
Vicat softening temperature  VST/A50(10N)	°C	ISO 306	154
Other Properties
Density	g/cm3	ISO 1183	0.91

 

Properties	Unit	Test method	Value
Melt Flow Rate
Melt flow rate(230°C/2.16KG)	g/10min	ISO 1133	12
Mechnical Properties
Tensile modulus of elasticity(v=1mm/min)	Mpa	ISO 527-2	1550
Tensile yield at stress(v=50mm/min)	Mpa	ISO 527-2	35
Tensile yield at strain (v=50mm/min)	%	ISO 527-2	8
Tensile strain at break (v=50mm/min)	%	ISO 527-2	>50
Charpy impact strength unnotched(+23°C)	kJ/m2	ISO 179/1eU	110
Charpy impact strength notched(+23°C)	kJ/m2	ISO 179/1eA	3.0
Izod Impact strength notenched(+23°C)	kJ/m2	ISO 180/1A	3
Ball indentation hardness(H 358/30)	Mpa	ISO 2039-1	78
Thermal Properties
Melting point,DSC	°C	ISO 3146	163
Heat deflection temperature (0.45Mpa)	°C	ISO 75-2	85
Vicat softening temperature  VST/A50(10N)	°C	ISO 306	154
Other Properties
Density	g/cm3	ISO 1183	0.91

PP Yarn Grade, PP raffia Grade

ITEM	Unite	Value
Melt Mass-Flow Rate (MFR, 2.16kg)	g/10 min≤	3.2
Density	Kg/m3	915
Tensile Strength at Break	MPa≥	35
Flexural Modulus	MPa≥	1550
IZOD Impact Strength(23ºC)	J/M	55
Rockwell hardness	R	102
Vicat softening point(10N)	°C	156
Distortion Temperature	°C	95

PP injection grade

ITEM	Unite	Value	Test Method
Melt Mass-Flow Rate (MFR, 2.16kg)	g/10 min	8	ASTM D-1238
Tensile Strength at Yield (50 mm/min)	MPa	23	ASTM D-638
Elongation at Yield (50 mm/min)	%	7	ASTM D-638
Flexural Modulus (1% secant)	MPa	1050	ASTMD-790A
Notched Izod Impact Strength (23°C)	J/m	150	ASTM D-256
Heat Deflection Temperature (455 kPa)	°C	95	ASTM D648

PP film grade

ITEM	Unite	Value	Test Method
Melt Mass-Flow Rate (MFR, 2.16kg)	g/10 min≤	12.3	GB/T 3682
Tensile Strength at yield	MPa≥	30.8	GB/T 1040
Bending modulus	≥	1000	GB/T 9341
Notched Izod impact Strength	(23ºC, KJ/m2)	9.2	GB/T 1843

PP Pipe Grade

ITEM	Unite	Value	Test Method
Melt Mass-Flow Rate	g/10 min	40	GB3682
Density	kg/m3	905	ASTM/D1505
Tensile Strength at Yield	MPa	23	GB1040
Tensile Elongation at Break	%	50	GB1040
Rockwell Hardness		85	GB9342
Heat Deflection Temperature	ºC	105	ASTM/D648
IZOD Impact Strength	(23ºC,J/m)	60	ASTM/D265

Contact us if you need more details on Virgin PP Granules. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Recycled PP Granules、PP Resin. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Plastic Materials